A satin finish polyurethane varnish designed primarily for interior use.
Resistant to hot water, mild acids and alkalis. The quick drying
formulation minimises dust contamination. |
|
|
Colour |
YVA251-Clear |
|
Finish |
Satin |
|
Specific Gravity |
0.9 |
|
Volume Solids |
46% |
|
Typical Shelf Life |
2 yrs |
|
VOC (As Supplied) |
425 g/lt |
|
Unit Size |
375 ml 750 ml 2.5 Lt |
|
| |
Drying |
|
5ºC |
15ºC |
23ºC |
35ºC |
|
|
|
Touch Dry [ISO] |
5hrs |
3hrs |
1hrs |
30mins |
| |
Overcoating |
| |
Substrate Temperature |
| |
5ºC |
15ºC |
23ºC |
35ºC |
|
Overcoated By |
Min |
Max |
Min |
Max |
Min |
Max |
Min |
Max |
|
|
|
Goldspar Satin |
24hrs |
4days |
15hrs |
3days |
6hrs |
2days |
3hrs |
1days |
|
|
Preparation |
PREVIOUSLY VARNISHED WOOD:
In Good Condition: Clean with thinners. Sand smooth with 280-320
grade paper. Remove sanding dust with thinners.
In Poor Condition: Remove all previous coatings.
BARE WOOD: Sand smooth with 80-180 grade paper and then 280 grade
paper. Remove sanding dust by brushing, dusting and wiping. If wiping
with solvent then allow to dry completely before applying the first
coat.
Priming bare wood:: Apply Intertox or UCP. If UCP has been
omitted thin the first coat by 10-15% with Thinners No.1. |
|
|
|
Method |
Apply a minimum of 3 unthinned coats, more if using a roller. |
|
|
|
Hints |
Mixing Stir well before use.
Thinner YTA800,YTA085 Thinners No.1 Thinners No.3
Cleaner YTA800 Thinners No.1
Airless Spray Pressure: 176-210 bar. Tip Size: 1365-1580.
Conventional Spray Pressure: 2-3 bar. Tip Size: 1.1-1.4 mm. Thin
25-30% with Thinners No.3
Roller If applying by roller, lay off with a brush or pad
otherwise air bubbles may become trapped in the film.
Other For Airmix spray application: Pressure: 2 bar. Tip Size:
06-113. For best results sand lightly between coats with 320-400 grade
paper. Avoid using direct from the can. Pour the amount you expect to
use in a separate container. For a particularly clear finish, use
Goldspar Satin for the final coat only and Goldspar for the first 2 to 3
coats. |
|
|
|
Some Important Points |
Only use recommended thinners. Use above the waterline only. Avoid
painting in direct sunlight. Product temperature should be minimum 15°C
and maximum 35°C. Ambient temperature should be minimum 5°C/40°F and
maximum 35°C/95°F. Substrate temperature should be minimum 5°C/40°F and
maximum 35°C/95°F. |
|
|
|
Compatibility/Substrates |
Suitable for use on all types of wood except direct application on oily
timbers such as Teak and Iroko. |
|
|
|
Number of Coats |
3 minimum |
|
|
|
Coverage |
(Theoretical) - 10.30 (m²/lt) |
|
|
|
Recommended DFT |
40 microns dry by brush
|
|
Recommended WFT |
87 microns wet by brush |
|
|
|
Application Methods |
Brush, Roller, Conventional Spray, Airmix, Airless Spray |
|
|
Storage |
GENERAL INFORMATION:
Exposure to air and extremes of temperature should be avoided. For the
full shelf life of Goldspar Satin to be realised ensure that between use
the container is firmly closed and the temperature is between 5°C/40°F
and 35°C/95°F. Keep out of direct sunlight.
TRANSPORTATION:
Goldspar Satin should be kept in securely closed containers during
transport and storage.
|
|
|
|
Safety |
GENERAL: Read the label safety section for Health and Safety
Information, also available from our Technical Help Line.
DISPOSAL: Do not discard tins or pour paint into water courses, use the
facilities provided. It is best to allow paints to harden before
disposal.
Remainders of Goldspar Satin cannot be disposed of through the municipal
waste route or dumped without permit. Disposal of remainders must be
arranged for in consultation with the authorities.
|
|
|
IMPORTANT NOTES |
The information given in this sheet is not intended to be exhaustive.
Any person using the product without first making further written
enquiries as to the suitability of the product for the intended purpose
does so at their own risk and we can accept no responsibility for the
performance of the product or for any loss or damage (other than death
or personal or injury resulting from negligence) arising out of such
use. The information contained in this sheet is liable to modification
from time to time in the light of experience and our policy of
continuous product development. |
|